Method and structure of converging electron-emission source of field-emission display

ABSTRACT

A method and a structure for a converging-type electron-emission source of a field-emission display are disclosed. A substrate is provided, and a silver paste is used to form a first electrode layer on the substrate by the process such as thick-film photolithography or screen-printing. A carbon nanotube is formed on the first electrode layer by thick-film photolithography or screen-printing, and a second electrode is formed on the carbon nanotube. A third electrode layer is formed on the first electrode layer around the second electrode layer by thick-film photolithography or screen-printing. The third electrode layer is higher than the second electrode layer, such that a converging exit is formed around the second electrode layer. A sintering step is performed. When the electron beam is generated, the electron beam is concentrated at the center of the converging exit to impinge a phosphor layer of an anode without causing gamut.

BACKGROUND OF THE INVENTION

The present invention relates in general to a structure and a method for forming a converging-type electron-emission source of a field-emission display, and more particularly, to a method of forming a recessed region or a slot in a cathode structure and a carbon nanotube in the recessed region, such that the peripheral electrode layer protrudes over the electron-emission source. In addition, the protruding electrode layer forms the potential distribution to achieve converging effect of the electron beam.

In the conventional bipolar or tri-polar field-emission display having a carbon nanotube as an electron-emission source (as shown in FIGS. 1 and 2), the electrons are drained from the electron-emission source to impinge the phosphor layer of the anode, so as to excite the phosphor to illuminate. The configuration of the cathode and anode often causes the electron beams diverged due to the electric field. Sometimes the electron beams may even impinge the phosphor of the neighboring anode unit to cause gamut. The image display by such display is thus seriously degraded.

To resolve the electron-beam diffusion problem of the conventional bipolar or tri-polar field-emission display, tetra-polar (as shown in FIG. 3) or penta-polar field-emission display has been proposed. The tetra- or penta-polar field-emission display has a converging electrode layer in addition to the basic components of the bi- or tri-polar field-emission display. Therefore, the electron emission generated from the cathode can be focused or converged into a concentrated beam to precisely and sufficiently impinge the phosphor of the corresponding anode unit. Thereby, gamut is prevented to appear in the image.

The converging electrode layer formed between the cathode structure and the anode structure of a tetra-polar field-emission display provides a voltage to converge the electron beam. The fabrication process of this type of tetra-polar field-emission display includes forming a converging electrode layer on a gate electrode layer by photolithography, or forming a shadow mask between the cathode and anode structures to serve as the converging electrode layer. Either type of converging electrode layer does not only increase the complexity of fabrication, but also increase the material cost.

BRIEF SUMMARY OF THE INVENTION

It is therefore a substantial need for redesigning the cathode structure of a field-emission display without causing extra fabrication process and cost. The redesign of the cathode structure provides a converging electrode layer that does not require extra circuit control, while the fabrication process is simplified, and material cost is greatly reduced. By the redesign of the cathode structure as provided, the electron beam generated by the electron-emission source is converged and concentrated to precisely impinge the phosphor of the corresponding anode unit.

The method as provided includes forming a first electrode layer on a glass substrate, and a second electrode layer and a third electrode layer on the first electrode layer. The second electrode layer serves as an electron-emission layer surrounded by the third electrode layer. The third electrode layer is higher the second electrode layer, such that a converging opening is formed for the electrons generated by the second electrode layer.

The first and third layers are preferably fabricated from silver ink by thick-film photolithography or screen-printing process, and carbon nanotube is preferably used for forming the second electrode layer.

The cathode structure of a field-emission display as provided includes a first electrode, and a second electrode and a third electrode layers formed on the first electrode layers. The third electrode layer is higher than the second electrode layer and encompasses the second electrode layer therein. Thereby, a converging opening is formed by the electrode potential of the third electrode layer over the second electrode layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The above objects and advantages of the present invention will be become more apparent by describing in detail exemplary embodiments thereof with reference to the attached drawings in which:

FIG. 1 shows a conventional bipolar field-emission display;

FIG. 2 shows a conventional tri-polar field-emission display;

FIG. 3 shows a conventional tetra-polar field-emission display;

FIGS. 4-7 shows the fabrication process of a cathode structure of a field-emission display in one embodiment of the present invention;

FIG. 8 shows the a single cathode unit of a field-emission display provided by the present invention; and

FIG. 9 shows the emission of electrons generated by the cathode structure of the field-emission display provided by the present invention.

DETAILED DESCRIPTION OF THE INVENTION

Referring to FIGS. 4-7, the fabrication process of the cathode structure of a field-emission display is illustrated. The fabricated process as provided includes a step of forming recessed region in the cathode structure, and a step of forming the electron-emission source in the recessed region. The electron-emission source includes carbon nanotube, for example. Thereby, the peripheral electrode layer on the periphery of the electron-emission source is higher than the electron-emission source, such that a potential distribution causes the electron beam generated by the electron-emission source to be converged.

While fabricating the cathode structure 10 of the field-emission display, a glass substrate 1 provided. A first electrode layer 2 is formed on the substrate 1. The method for forming the first electrode layer 2 includes thick-film photolithography or screen-printing. The thickness of the first electron layer 2 is about 10 microns to 20 microns, and the material for forming the first electrode layer 2 includes silver paste, for example.

A second electrode layer 3 is then formed on the first electrode layer 2 by thick-film photolithography or screen-printing, for example. The material for forming the second electrode layer 3 is an electron-emission source such as a carbon nanotube, and the thickness of the second electrode layer is about one micron to about 5 microns, for example.

A thick-film photolithography process or a screen-printing process is performed to form a third electrode layer 4 on the first electrode layer 2. The third electrode layer 4 is formed encircling the second electrode layer 2 therein. Silver glue or ink can be used for forming the third electrode layer 4, for example. The thickness of the third electrode layer 4 is about 10 microns to about 40 microns. Therefore, a converging opening 5 is formed over the second electrode layer 3 encircled by the third electrode layer 4. The thickness of the third electrode layer 4 or the internal diameter of the converging opening 5 can be adjusted to optimize the converging effect.

When the third electrode layer 4 is formed, a sintering process is performed on the cathode structure 10.

FIGS. 8 and 9 show a single cathode unit and the electron beam generated by the cathode unit. As shown, the cathode unit is has a first electrode layer 2 formed on the glass substrate 1, a second electrode layer 3, which is an electron-emission layer, formed on the first electrode layer 2, and a third electrode layer 4 formed on the first electrode layer 2 surrounding the electron-emission layer 3. The third electrode layer 4 is higher than the second electrode layer 3, such that a converging opening 5 is formed by the third electrode layer 4 over the second electrode layer 3.

When a voltage is applied to the field-emission display 10 to excite an electron beam from the second electrode layer 3, the converging opening 5 formed by the third electrode layer 4 causes the electron beam to be concentrated, such that the electron beam can precisely impinge the phosphor layer of the corresponding anode unit without causing gamut.

Therefore, the electron-emission source of the field-emission display has at least the following advantages:

-   -   (1) Electrons drained form the electron source of the cathode         structure are converged by the configuration of and electric         field induced by the third electrode layer;     -   (2) The concentration effect is advantageous for providing         uniform distribution of the electron beam; and     -   (3) Low-cost thick-film process can be used for forming the         converging-type electron emission source, such that the cost for         fabricating the field-emission display can be reduced.

While the present invention has been particularly shown and described with reference to preferred embodiments thereof, it will be understood by those of ordinary skill in the art the various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the appended claims. 

1. A method of forming a converging-type electron-emission source of a field-emission display, comprising: providing a substrate; performing thick-film or screen-printing process to form a first electrode layer on the substrate; performing a thick-film or screen-printing process to form a second electrode layer and a third electrode layer on the first electrode layer, wherein the third electrode layer encompassing the second electrode therein and has a height higher than that of the second electrode layer, such that a converging opening is formed over the second electrode layer; and performing a sintering process.
 2. The method of claim 1, wherein the step of providing a substrate includes a step of providing a glass substrate.
 3. The method of claim 1, wherein the step of forming the first electrode layer includes using silver ink to form the first electrode layer.
 4. The method of claim 3, wherein the step of forming the first electrode layer includes forming the first electrode layer with a thickness of about 10 to 20 microns.
 5. The method of claim 1, wherein the step of forming the second electrode layer includes using carbon nanotube for forming the second electrode layer.
 6. The method of claim 5, wherein the step of forming the second electrode layer includes forming the second electrode layer with a thickness of about one to five microns.
 7. The method of claim 1, wherein the step of forming the third electrode layer includes using silver ink to form the third electrode layer.
 8. The method of claim 7, wherein the third electrode layer is formed with a thickness of about 10 to 40 microns.
 9. The method of claim 1, further comprising adjusting thickness of the third electrode layer or varying an internal diameter of the converging opening to adjust a converging effect.
 10. A converging electron-emission source of a field-emission display, comprising: a substrate; a first electrode layer formed on the substrate; a second electrode layer formed and patterned on the first electrode layer; a third electrode layer formed on the first electrode layer around the second electrode layer therein, wherein the third electrode layer is higher than the second electrode layer to form a converging opening over the second electrode layer.
 11. The electron-emission source of claim 10, wherein the substrate includes a glass substrate.
 12. The electron-emission source of claim 11, wherein the first and third electrode layers are fabricated from silver ink.
 13. The electron-emission source of claim 11, wherein the second electrode layer is fabricated from carbon nanotube.
 14. A field-emission display, comprising a plurality of pairs of anode units and cathode units, wherein each of the cathode unit comprises: a first electrode layer; a second electrode layer formed on the first layer to serve as an electron-emission layer; and a third electrode layer formed on the first layer around the second electrode layer, the third electrode layer being higher than the second electrode layer, such that a converging opening is formed by the third electrode layer over the second electrode layer.
 15. The display of claim 14, wherein the second electrode layer includes a layer of carbon nanotube. 